Product Name: |
Permanent Ferrite Magnet |
Application: |
Fan Starter Motor |
Shape: |
Arc,Tile |
Type: |
Anisotropic Sintered Magnet |
Composite: |
Ferrite Strontium Powder |
Size: |
(R16.0mm-r12.1mm)×18mm |
Processing: |
Wet Pressed |
Package Size: |
340mm×255mm×75mm |
Quantity Per Carton: |
840pcs |
Coating: |
No Coating |
Product Name: |
Permanent Ferrite Magnet |
Application: |
Fan Starter Motor |
Shape: |
Arc,Tile |
Type: |
Anisotropic Sintered Magnet |
Composite: |
Ferrite Strontium Powder |
Size: |
(R16.0mm-r12.1mm)×18mm |
Processing: |
Wet Pressed |
Package Size: |
340mm×255mm×75mm |
Quantity Per Carton: |
840pcs |
Coating: |
No Coating |
Strong Magnetic Ringv Sintered High Temperature Ferrite Magnets For Fan Starter Motors W1104
What does Xinheng offer to customers?
Our company manufactures an-isotropic ceramic strontium ferrite magnet made by means of wet compression molding.
What's the feature of ceramic strontium ferrite magnet made by wet compression molding?
Composition - Contain strontium ferrite (SrFe12O19) as the primary magnetic material. Strontium ferrite has good magnetic properties and is inexpensive to produce.
Density - Have a high relative density of around 95% or more after sintering. This gives good mechanical strength.
An-isotropy - Exhibit strong magnetocrystalline an-isotropy due to their hexagonal crystal structure. This results in a preferred direction of magnetization along one axis.
Particle shape - The strontium ferrite powder used typically has a hexagonal platelet morphology which helps promote magnetic an-isotropy during molding and sintering.
Molding method - The powder is mixed with a liquid binder and compression molded into a dense green compact using high pressures. This orients the an-isotropic particles.
Firing process - The compact is then sintered at high temperature to develop density while preserving the induced magnetic anisotropy orientation from molding.
Remanence - Have a maximum magnetic flux density or remanence along the axis of anisotropy, but little/no remanence perpendicular to it.
Coercivity - Usually have medium to high coercivity depending on additives, density, and anisotropy level achieved.
PHYSICAL PROPERTIES OF SINTERED FERRITE MAGNETS
Units | Sintered Ferrite (Ceramic) | |
Curie Temperature | ºC | 450 |
Maximum Operating Temperature | ºC | 350 |
Hardness | Hv | >530 |
Density | g/cm3 | 4.8 – 5.0 |
Relative recoil permeability | μrec | 1.05-1.1 |
Temperature Coefficient Br | %/ºC | -0.18 |
Temperature Coefficient iHc | %/ºC | 0.11-0.40 |
Anti-Bending Strength | N/m2 | (0.5-0.9)×108 |
Anti-Compressive Strength | N/m2 | ≥6.9×108 |
Anti-Tensile Strength | N/m2 | (0.2-0.5)×108 |
Specific Heat | J/kg·K | 600-900 |
Resistivity | Q.cm | >104 |
What's the application of Xinheng's permanent ferrite magnets?
Xinheng mainly manufactures the following types of ceramic arc segment magnets:
How Xinheng fabricates its permanent strontium ferrite magnet?
FERRITE POWDER GRADE OF MOTORCYCLE MOTORS MAGNET
牌号 Grade |
Br(mT) | Hcb(KA/m) | Hcj(KA/m) | (BH)max(KJ/m3) | ||||
mT | Gs | KA/m | Oe | KA/m | Oe | KJ/m3 | MGOe | |
Y33 | 410-430 | 4100-4300 | 220-250 | 2760-3140 | 225-255 | 2830-3200 | 31.5-35.0 | 3.9-4.4 |
Y33H | 410-430 | 4100-4300 | 250-270 | 3140-3390 | 250-275 | 3140-3450 | 31.5-35.0 | 3.9-4.4 |
Y33H-2 | 410-430 | 4100-4300 | 285-315 | 3580-3960 | 305-335 | 3830-4200 | 31.8-35.0 | 4.0-4.4 |
Y34 | 420-440 | 4200-4400 | 200-230 | 2510-2890 | 205-235 | 2570-2950 | 32.5-36.0 | 4.1-4.4 |
Y35 | 430-450 | 4300-4500 | 215-239 | 2700-3000 | 217-241 | 2730-3030 | 33.1-38.2 | 4.1-4.8 |
Y36 | 430-450 | 4300-4500 | 247-271 | 3100-3400 | 250-274 | 3140-3440 | 35.1-38.3 | 4.1-4.8 |
Y38 | 440-460 | 4400-4600 | 285-305 | 3580-3830 | 294-310 | 3690-3890 | 36.6-40.6 | 4.6-4.8 |
Y40 | 440-460 | 4400-4600 | 330-354 | 4150-4450 | 340-360 | 4270-4520 | 37.6-41.8 | 4.7-5.2 |
MOTORCYCLE MOTORS MAGNET SPECIFICATION TABLE
No. | Item | R | r | W | L | h | Grade | Application |
1 | W118 | 68.1 | 60.7 | 25 | 25 | 7.50 | Y33H | 1KW inverter motor |
2 | W018F | 72.5 | 60.7 | 27.9 | 35 | 11.80 | Y40 | 2KW inverter motor |
3 | W005A | 72.5 | 60.5 | 29.5 | 42 | 11.80 | Y33H | 2.3KW inverter motor |
4 | W050E | 87.3 | 78.5 | 24 | 40 | 8.80 | Y33H | 2.6KW inverter motor |
5 | W159 | 74.1 | 65.5 | 28.86 | 47 | 8.60 | Y40 | 2.8KW inverter motor |
6 | W017F | 86.5 | 78.5 | 24.0 | 51 | 7.90 | Y33H-2 | 3KW inverter motor |
7 | W087 | 86.5 | 78.5 | 24.0 | 64 | 7.80 | Y33H-2 | 5KW inverter motor |
8 | W138C | 101 | 90.2 | 24.5 | 65 | 10.8 | Y40 | 7KW inverter motor |
9 | W019B | 112 | 100 | 28.5 | 60 | 11.90 | Y40 | 9KW inverter motor |
Introduction Of Fan Motor:
Rotor Magnet: Permanent magnet ferrites are used as magnets in the rotor of fan motors. The rotor is the rotating part of the motor that is connected to the fan blades. Ferrite magnets provide a strong and stable magnetic field when an electric current passes through the stator coils, creating a force that causes the rotor to rotate.
Motor Efficiency: Permanent magnet ferrites contribute to the efficiency of fan motors. They offer high magnetic properties, such as a high coercivity and strong magnetic field, which allow for efficient energy conversion from electrical to mechanical energy. This results in improved motor performance and energy efficiency.